WC-Co Tungsten Carbide Coatings. WC-Co (88-12 Co)

  • HVAF and HVOF WCCo tungsten carbide coatings exhibit excellent resistance to sliding wear, abrasion, and erosion but slight lower corrosion resistance than WCCoCr.
  • HVAFWCCothermal spray coatings are non-permeable to gas and liquid at even 50 microns.
  • Tungsten carbide WC-12Co layers are resistant to sliding wear, impact, abrasion and fretting at temperatures up to 510ºC, preferably in non-corrosive media. We offer chromium carbide coatings for elevated temperature application.
  • This HVOF or HVAF tungsten carbide coatings can be used in a dry non-corrosive environment in India.

HVOF and HVAF WCCo coatings

  • HVOF technology is generally used for WC coating application sometimes generates material oxidation and decomposition of WC feedstock materials during in-process HVOF deposition. It is directly related to the high combustion temperature which is more than 3000ºC as well as the presence of oxygen in HVOF combustion products. These usually result in coating embrittlement and further reduction of service life in the condition of abrasive and erosive wear.
  • For tungsten carbide based powders, particle velocity exceeds 700-900 m/s, while particle surface temperature remains about 100˚c below the melting point of the metallic binder, allowing HVAF equipment to operate in a “solid-particle” spray mode. The latter is possible due to the relatively low combustion temperature of air-gaseous fuel mixtures at 3.5 – 4.5 bar chamber pressure.
  • The result is a formation of coatings with extremely low oxygen content as well as little, if any, thermal deterioration of carbides. Improved toughness, cohesion and low residual stresses in the HVAF sprayed layers permits routine deposition of thick carbide coatings, the superfinishing of coatings to an optical mirror, as well as result in noticeable improvement of fatigue resistance of the coatings.
  • HVAF combustion temperature below 2000°C, the surface temperature of cobalt and chromium alloy particles usually remains near their melting point.
  • A characteristics feature of HVAF process is that particles are heated gently and not fused during spraying.
  • Uniformly high hardness and ductility, low stress and porosity result in substantial increase service life of parts protected with HVAF WC-Co coatings in comparison with HVOF tungsten carbide versions.

WCCo 88/12 Powder Properties

Nominal Composition Wt.%
Tungsten Carbide Base
Total Carbon 5.3 – 5.4
Cobalt 11–13

Powders are available on the market where cobalt is replaced with nickel.

Properties

Feature S.I. Unit
Apparent metallographic porosity <0.1
Bond strength of tungsten carbide coating to carbon PSI 12,000+
hardness range, HV300 1150-1600
hardness deviation from a target value, HV300 ±60
typical as-sprayed roughness Ra, microns 3
maximum coating thickness, mm 3
maximum working temperature of the coating, °C 510
micrograph of the WCCo

Micrograph of the WCCo 88-12 Thermal Spray Coating

Typical Applications of WCCo coatings in India

  • Steel rolls.
  • Corrugated rolls.
  • Sucker rods.
  • Exhaust fans.
  • Conveyer screws.

Endurance Wear Solutions Llp thermal spray HVOF and HVAF WCCo coatings at our shop in Mumbai, Maharashtra, India. Call us or send an inquiry to get our best price.